Fused Magnesium

Description of Fused Magnesium

Fused Magnesium(FM) is a type of refractory material that is produced by the electric arc melting of caustic calcined magnesia, deadburned magnesia or raw magnesite in furnaces at temperatures in excess of 2750°C. It has a high melting point, excellent thermal shock resistance, and good chemical stability, making it a popular choice for use in a variety of industrial applications such as steelmaking, cement manufacturing, and glass production.

Kerui Fused Magnesium Technical Data Sheet

Product	MgO	SiO2	Al2O3	Fe2O3	CaO	Loi	BD	Paquete
Name	(%)	(%)	(%)	(%)	(%)	(%)	(kg/cm3)
FM94	94MIN	2.5MAX	0.6MAX	1.0MAX	2.0MAX	0.3MAX	3.4MIN	TON BAG (1.25)
FM95	95MIN	1.5MAX	0.6MAX	1.0MAX	2.0MAX	0.3MAX	3.4MIN	TON BAG (1.25)
FM96	96MIN	0.9MAX	0.2MAX	0.8MAX	1.2MAX	0.2MAX	3.45MIN	TON BAG (1.25)
FM97	97MIN	0.7MAX	0.2MAX	0.8MAX	1.2MAX	0.2MAX	3.48MIN	TON BAG (1.25)
FM98	98MIN	0.5MAX	0.15MAX	0.5MAX	1.0MAX	0.1MAX	3.48MIN	TON BAG (1.25)
Coarse Sizes		1-15 mm, 3-15 mm, 5-15 mm, 3-8 mm, 5-10 mm, customizable
Small Fractions		0-1 mm, 0.5-1 mm, 1-3 mm, 1-5 mm, 200 mesh, customizable
Packing		1.35 Ton Bags, customizable
Colour		Brown		Blanco		Large crystal

OBTENER PRECIO

Fused Magnesia Production Process:

Magnesite (magnesium carbonate MgCO3) is converted into magnesia by the application of heat which drives off carbon dioxide (CO2), thereby converting the carbonate to the oxide of magnesium (MgO).

Fused magnesia is a high-purity material used in the production of refractory materials, ceramics, and other industrial applications. The production of fused magnesia involves several steps.

Raw Material Preparation: The raw material used in the production of fused magnesia is magnesite, a natural mineral. The magnesite is first crushed into small pieces and then calcined at high temperatures to remove impurities and water.

Fusion: The calcined magnesite is then mixed with coke and other additives and fed into an electric arc furnace. The furnace is heated to a temperature of around 3,000 degrees Celsius, causing the magnesite to fuse into a molten state.

Cooling and Solidification: The molten magnesia is then cooled and solidified by pouring it into molds or by spraying it with water. This process can take several days or even weeks, depending on the size and shape of the desired product.

Applications of Fused Magnesium

Fused Magnesium (FM) Application:

– High performance Ladrillo de carbón de magnesia for steel industry,

– Fired refractory bricks for cement and glass industry,

– Heating elements industry